Ngwakọta nke e ji aka mee ka ọ dị ike nke phenolic 4330-3 Shunds
Nkọwa Ngwaahịa
4330-3, a na-ejikarị ngwaahịa a eme ihe maka ịkpụzi, mmepụta ike, ụgbọ okporo ígwè, ụgbọelu, na ụlọ ọrụ ndị ọzọ eji eme ihe abụọ, dị ka akụkụ igwe, nwere ike igwe dị elu, mkpuchi dị elu, okpomọkụ dị elu, obere iguzogide nchara okpomọkụ na njirimara ndị ọzọ.
Ngwaahịa a bụ ihe e ji kpụọ thermosetting nke e ji phenolic resin ma ọ bụ resin ya agbanwere agbanwe mee dị ka ihe na-ejikọ ya, ya na eriri eriri iko na-enweghị alkali na ihe mgbakwunye ndị ọzọ.
Nkọwapụta Ngwaahịa
| Ụkpụrụ Ule | JB/T5822- 2015 | |||
| Mba. | Ihe Nnwale | Ngalaba | BH4330-1 | BH4330-2 |
| 1 | Ọdịnaya Resin | % | A pụrụ ịkparịta ụka | A pụrụ ịkparịta ụka |
| 2 | Ọdịnaya Ihe Na-agbanwe Agbanwe | % | 4.0-8.5 | 3.0-7.0 |
| 3 | Njupụta | g/cm3 | 1.65-1.85 | 1.70-1.90 |
| 4 | Mmịpụta Mmiri | % | ≦0.2 | ≦0.2 |
| 5 | Okpomọkụ Martin | ℃ | ≧280 | ≧280 |
| 6 | Ike ịgbagọ | MPa | ≧160 | ≧450 |
| 7 | Ike Mmetụta | KJ/m2 | ≧50 | ≧180 |
| 8 | Ike ọdụdọ | MPa | ≧80 | ≧300 |
| 9 | Nguzogide Elu | Ω | ≧10×1011 | ≧10×1011 |
| 10 | Nguzogide Olu | Ω.m | ≧10×1011 | ≧10×1011 |
| 11 | Ihe na-eyi uwe dị n'etiti (1MH)Z) | - | ≦0.04 | ≦0.04 |
| 12 | Ikike Ndị Dị Mkpa (1MHZ) | - | ≦7 | ≦7 |
| 13 | Ike Dielectric | MV/m | ≧16.0 | ≧16.0 |
Storge
E kwesịrị ịchekwa ya n'ime ụlọ kpọrọ nkụ ma nwee ikuku ebe okpomọkụ anaghị agafe 30℃.
Ekwula nso ọkụ, kpoo ọkụ ma ọ bụ ìhè anyanwụ kpọmkwem, kwụsie ike n'elu ikpo okwu pụrụ iche, a machibidoro ịtụnye ihe n'ahịrị kwụ ọtọ na nrụgide dị arọ kpamkpam.
Ndụ nchekwa bụ ọnwa abụọ site na ụbọchị emepụtara ya. Mgbe oge nchekwa gasịrị, a ka nwere ike iji ngwaahịa ahụ mgbe emechara nyocha ahụ dịka ọkọlọtọ ngwaahịa si dị. Ọkọlọtọ teknụzụ: JB/T5822-2015